Portadur P2
Portadur P2 is a high gold, palladium-free casting alloy with a warm golden colour. The mechanical and physical properties of this alloy allow the production of even long-span restorations.
Indications*
- Inlays
- Onlays, 3/4 crowns, crowns
- Telescope crowns, conus crowns
- Bridges
- Wide-span bridges
- Cast posts / cores, bars, attachments
- Implant-supported superstructures
- Partial dentures
Technical Data
| Composition (%): | Au 71.0 | Ag 12.2 | Cu 12.2 | Pt 2.5 | Pd 1.5 | Zn <1.0, Ir <1.0 |
| ISO | 22674:2016 |
| Type / Color | 4 / Rich Yellow |
| Density (g/cm³) | 15.5 |
| Melting Range (Solidus/Liquidus): | 890 - 930 °C |
| Elastic Modulus (GPa): | 100 |
| As Cast Softened Hardened | |
| Vickers Hardness: | 230 160 230 |
| Tensile Strength (MPa): | 670 490 700 |
| 0.2% Proof Stress (MPa): | 560 350 560 |
| Elongation (%): | 19 26 11 |
Advantages
- Good melting and flow properties
- Wide range of indications
- Veneering with laboratory composites (e.g. SR Nexco)
- Certified biocompatibility
Processing Data
| Investment Material: | Phosphate-bonded / Gypsum-bonded |
| Preheating / Burn- out Temperature: | 700 °C |
| Crucible | Carbon crucible / Ceramic crucible |
| Casting Temperature: | 1080 °C |
| Casting Temperature: | SR Nexco |
| Laser Welding Wire: | Portadur P2 |