Euro 33 Implant
Euro 33 Implant is a high strength ceramic alloy. This high strength together with high heat resistance allow accurately fitting casting objects to be produced, especially for implant-supported superstructures.
Indications*
- Crowns
- Telescope crowns, conus crowns
- Bridges
- Wide-span bridges
- Cast posts / cores, bars, attachments
- Implant-supported superstructures
- Partial dentures
Technical Data
| Composition (%): | Pd 43.9 | Au 28.0 | Ag 19.5 | Sn 4.8 | In 3.5 | Ru <1.0 |
| ISO | 22674:2016 |
| Type / Color | 4 / White |
| Density (g/cm³) | 12.3 |
| Melting Range (Solidus/Liquidus): | 1220 - 1290 °C |
| Elastic Modulus (GPa): | 113 |
| Porcelain Fired Hardened | |
| Vickers Hardness: | 230 260 |
| Tensile Strength (MPa): | 720 760 |
| 0.2% Proof Stress (MPa): | 470 500 |
| Elongation (%): | 18 17 |
Advantages
- High mechanical strength
- Excellent processing and polishing properties
- Economical due to low density
- High heat resistance
- Compatible with conventional metal-ceramics (e.g. IPS Style)
Processing Data
| Investment Material: | Phosphate-bonded |
| Preheating / Burn- out Temperature: | 900 °C |
| Crucible | Ceramic crucible |
| Casting Temperature: | 1430 °C |
| Oxidation °C/min/Vacuum: | 950/5/Yes |
| CTE: | (25 – 500 °C): 14.3 x 10-6 /K |
| Recommended Metal Ceramic: | IPS Style, IPS InLine |
| Laser Welding Wire: | Porta P6 |
*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES