Duo Pal 6
Duo Pal 6 is a palladium-based ceramic alloy, compatible with conventional metal-ceramics. Its good heat resistance and excellent melting and flow properties enable easy processing up to polishing.
Indications*
- Crowns
- Telescope crowns, conus crowns
- Bridges
- Wide bridges
- Cast posts / cores, bars, attachments
- Implant-supported superstructures
- Partial dentures
Technical Data
| Composition (%): | Pd 75.0 | Ag 8.4 | Au 6.0 | Sn 3.5 | Ga 6.5 | Ru <1.0, Ge <1.0 |
| ISO | 22674:2016 |
| Type / Color: | 4 / White |
| Density (g/cm³) | 11.6 |
| Melting Range (Solidus/Liquidus): | 1110 - 1280 °C |
| Elastic Modulus (GPa): | 116 |
| Porcelain Fired Hardened | |
| Vickers Hardness: | 250 250 |
| Tensile Strength (MPa): | 770 770 |
| 0.2% Proof Stress (MPa): | 520 520 |
| Elongation (%): | 27 27 |
Advantages
- High heat resistance
- Excellent melting and flow properties
- Easy processing and polishing
- Wide range of indications
- Compatible with conventional metal-ceramics (e.g. IPS Style)
Processing Data
| Investment Material: | Phosphate-bonded |
| Preheating / Burn- out Temperature: | 900 °C |
| Crucible | Ceramic crucible |
| Casting Temperature: | 1400 °C |
| Oxidation °C/min/Vacuum: | 930 / 5 / No |
| CTE: | (25 – 500 °C): 14.1 x 10-6 /K |
| Recommended Metal Ceramic: | IPS Style, IPS InLine |
| Laser Welding Wire: | Porta P6 |
*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES
Instructions for Use