Advantages

• Minimized risk and improved calculability due to the fixed price strategy
• Low material consumption due to very low density and thus low fabrication costs per unit
• Excellent physical properties with high strength values, ideally suitable for the press technique
• Wide range of indications from single restorations to long-span bridges
• Compatible with the most popular veneering ceramics for the layering and press techniques as well as lab-composites

Indications

• Onlays
• ¾ crowns
• Crowns
• PFM crowns
• Short- and long-span bridges
• Telescopic- and conus crowns
• Posts
• Implant superstructures
• Partial dentures

Composition
Au    <1.0
Pd    24.6
Co    39.9
Cr    21.3
Mo    11.6
W    1.2
Fe    <1.0
Ta    <1.0
B    <1.0
Al    <1.0

Technical data
Typ                                                5
Colour                                          white
Density (g/m3)                           9.3
Melting range (°C)                     1185-1275
Casting temperature (°C)        1345-1385
CTE 25-500°C                           14.2
CTE 20-600°C                           14.6
Elongation (%)                            7.0
Modulus of elasticity (MPa)       230.000
Vickers hardness                       338
0.2% proof stress (MPa)           660